Technical data sheet |
|
VolgamidÒPA6G40TNC202
40%玻纖增強(qiáng)增韌尼龍6
40%glass fiber reinforced PA6 with flexibilizer |
|
項(xiàng)目Item |
典型性能Typical Characteristic |
測(cè)試標(biāo)準(zhǔn)Testing Standard |
|
值Value |
單位Unit |
|
機(jī)械性能Mechanical Properties |
|
|
|
|
拉伸強(qiáng)度Tensile Strength |
183 |
MPa |
ISO527, 50mm/min |
|
斷裂伸長(zhǎng)率Elongation at break |
2 |
% |
ISO527, 50mm/min |
|
彎曲強(qiáng)度Flexural Strength |
280 |
MPa |
ISO178, 2mm/min |
|
彎曲模量Flexural Modulus |
10800 |
MPa |
ISO178, 2mm/min |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度
Charpy Impact notched |
25 |
KJ/m2 |
ISO179/1eA |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度
Charpy Impact unnotched |
NB |
KJ/m2 |
ISO179/1eU |
|
洛氏硬度Rockwell Hardness |
|
|
ISO2039/2 |
|
熱性能Thermal Properties |
|
|
|
|
熱變形溫度
Temp. of deflection under load (0.45MPa) |
|
℃ |
ISO75 |
|
熱變形溫度
Temp. of deflection under load (1.80MPa) |
220 |
℃ |
ISO75 |
|
熔點(diǎn)Melting Point |
220 |
℃ |
ISO3146C |
|
電性能Electrical Properties |
|
|
|
|
體積電阻率Volume Resistant |
|
ohm*m |
IEC60093 |
|
表面電阻率Surface Resistant |
1013 |
ohm |
IEC60093 |
|
介電強(qiáng)度Dielectric Strength |
|
KV/mm |
IEC 60243-1 |
|
電痕化指數(shù)Comp Track Index |
|
V |
IEC 60112 |
|
其它Others |
|
|
|
|
密度Specific Gravity |
1.43 |
g/cm3 |
ISO1183 |
|
灰分Ash Content |
40±2 |
% |
ISO3451-4 |
|
熔體流動(dòng)速率（250℃,2.16kg）
Melt flow rate |
|
g/10min |
ISO62 |
|
吸水率Water Absorption |
1.5 |
% |
ISO62 |
|
吸濕率Humidity Absorption |
|
% |
ISO62 |
|
模塑收縮率Mold Shrinkage |
0.3/0.8 |
% |
ISO294-4 |
|
燃燒性能 |
|
|
|
|
UL垂直燃燒Flammability |
HB |
mm/Class |
UL-94 |
|
灼熱絲可燃指數(shù)
Glow-wire Flammability Index |
|
mm/℃ |
IEC 60695-2-12 |
|
Disclaimer：Unless specified to the contrary, the value given have been established on standardized test specimens at room temperature.The figures should be regarded as guide values only and not as binding minimum value. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the colouring. |
VOLGAMID 尼龍6增強(qiáng)增韌系列